Sustained coherent epitaxy and role of oxygen vacancies in La0.7Sr0.3MnO3−δ thin films grown on SrTiO3 by sputtering
Department of Physics, Polydisciplinary Faculty of Ouarzazate, Ibn Zohr University,
2 Department of Electronic Science and Engineering, Kyoto University, Kyoto 615-8510, Japan
* e-mail: firstname.lastname@example.org
Received in final form: 24 February 2021
Accepted: 21 May 2021
Published online: 16 June 2021
Ferromagnetic La0.7Sr0.3MnO3−δ (LSMO) epitaxial thin films of single-crystal quality with very smooth surfaces are grown on SrTiO3 (100) substrates by on-axis rf magnetron sputtering. We find that the resistivity and the spontaneous magnetization for these 180 nm thick films are nearly equal to those of single crystals after thermal annealing. On the other hand, the Curie temperature TC is no higher than 270 K, a value far below the bulk one, which is quite unusual. As a clue to this riddle, we note a strong correlation between the lattice constant for these films and the amount of oxygen vacancies in the case of LSMO, an oxygen-nonstoichiometric oxide. From this, we conclude that the sustained coherent epitaxy takes place to match the lattice mismatch of 0.8% by incorporating a limited amount of oxygen vacancies, which relaxes the film in-plane stress while functions to significantly reduce TC.
Note to the reader: Further to the publication of an erratum, the citation of the article was modified on 19 July 2021.
© EDP Sciences, 2021
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.