Hard magnetic properties of FePd nanoparticles*
1
Center for Materials Science, Department of Physics, Hanoi University of Science, VNU, 334 Nguyen Trai, Thanh Xuan, Hanoi, Vietnam
2
Nano and Energy Center, Vietnam National University, Hanoi, 334 Nguyen Trai, Thanh Xuan, Hanoi, Vietnam
a e-mail: namnh@hus.edu.vn
Received:
3
January
2013
Revised:
21
June
2013
Accepted:
12
July
2013
Published online:
4
October
2013
Magnetic nanoparticles FexPd100−x (x = 42, 50, 55, 60, 63) with small size of around 5–10 nm were prepared by sonochemistry from palladium acetate and iron acetate. The compositions x can be controlled by changing the ratio of the above precursor chemicals. Under the effect of annealing at various temperatures from 450 °C to 650 °C, structure change was observed and samples show hard magnetic properties with high coercivity up to 2.1 kOe. Magnetic properties of samples were then systematically discussed in dependence of x and annealing temperatures.
© EDP Sciences, 2013
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.