Optical and structural characterisation of Cu doped CdS (CdS:Cu) nanoparticles
Department of Physics, Faculty of Science, University of Guilan, P.O. Box 1914, Rasht, Iran
Corresponding author: firstname.lastname@example.org
Revised: 3 June 2010
Accepted: 7 June 2010
Published online: 2 August 2010
Cu doped cadmium sulfide (CdS:Cu) nanoparticles were prepared with a wet chemical synthesis by mixing the reactants in a double distilled water solvent. Thioglycerol (TG) was employed as the capping agent and also as the reaction catalyst. Properties of the particles were investigated using UV absorption; photoluminescence spectroscopy (PL) and X-ray diffraction analysis (XRD). The particle size of the prepared CdS:Cu nanoparticles was estimated to be about 4 nm. The XRD pattern of CdS:Cu nanoparticles reveals a hexagonal crystal structure at room temperature. Variation of the TG concentration does not shift the position of the excitonic peak in the absorption spectrum but the PL intensity increases as the TG concentration is increased. The PL intensity decreases with increasing Cu concentration.
© EDP Sciences, 2010
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.