Capacité de transport et de limitation du courant des matériaux YBaCuO texturés

L. Porcar; D. Bourgault; O. Belmont; J. G. Noudem; J. M. Barbut; M. Barrault; P. Tixador; X. Chaud; R. Tournier

doi:10.1051/epjap:1998111

All issues

Volume 1 / No 1 (January 1998)

Eur. Phys. J. AP, 1 1 (1998) 19-22

Abstract

Issue		Eur. Phys. J. AP Volume 1, Number 1, January 1998


Page(s)		19 - 22
DOI		https://doi.org/10.1051/epjap:1998111
Published online		15 January 1998

Eur. Phys. J. AP 1, 19-22 (1998)
https://doi.org/10.1051/epjap:1998111

Capacité de transport et de limitation du courant des matériaux YBaCuO texturés^*

Melt textured YBaCuO transport current capability. Application to current limitation

L. Porcar¹, D. Bourgault², O. Belmont¹, J. G. Noudem¹, J. M. Barbut¹, M. Barrault¹, P. Tixador³, X. Chaud² et R. Tournier²

¹ Schneider Electric S.A. Usine A, rue Volta, 38050 Grenoble Cedex 9, France
² CNRS-EPM/Matformag, B.P. 166, 38042 Grenoble Cedex 09, France
³ CNRS-CRTBT/LEG, B.P. 166, 38042 Grenoble Cedex 09, France

Auteur de correspondance : porcar@labs.polycnrs-gre.fr

Reçu : 13 Juin 1997
Accepté : 7 Octobre 1997
15 Janvier 1998

Résumé

Afin de déterminer la capacité à limiter le courant du composé ${\rm Y}_1{\rm Ba}_2{\rm Cu}_3{\rm O}_{7-\delta}$ texturé, des études en courants de transport élevés, en régime pulsé et en régime permanent alternatif, ont été menées. Il en résulte que YBaCuO possède une forte capacité de transport du courant en régime pulsé (9000 A soit 23 000 $\ {\rm A} / {\rm cm}^2$ dans un barreau de 4 cm de long) et en régime permanent alternatif (3000 A soit 7800 $\ {\rm A} / {\rm cm}^2$ ) et que le retour à l'état normal par dépassement du courant critique est très abrupt.

Abstract

Pulsed and permanent sinusoidal transport current have been applied to melt textured ${\rm Y}_1{\rm Ba}_2{\rm Cu}_3{\rm O}_{7-\delta}$ in order to estimate its current limitation capability. High pulsed transport currents reaching 9000 A (23 000 $\ {\rm A} / {\rm cm}^2$ ) crossed a 4 cm long sample. In permanent sinusoidal current, 3000 A (7800 $\ {\rm A} / {\rm cm}^2$ ) crossed the sample without showing any resistive losses. Above the critical current, the transition from the superconducting to the normal state is strongly abrupt.

PACS : 74.60.J – Critical currents / 81.10.H – Zone melting and zone refining / 81.40.R – Electrical and magnetic properties

^*

Le contenu de cet article a été présenté aux 4es journées d'étude SEE "Matériaux Supraconducteurs à haute T_c" de Caen, les 26 et 27 mars 1997.

Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.

Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.

Initial download of the metrics may take a while.

Capacité de transport et de limitation du courant des matériaux YBaCuO texturés*

Melt textured YBaCuO transport current capability. Application to current limitation

Capacité de transport et de limitation du courant des matériaux YBaCuO texturés^*