Thermally stimulated current measurements on polycrystalline PbI2 layers
Laboratoire PHASE (CNRS UPR 292),
BP 20, 67037 Strasbourg-Cedex 2, France
Corresponding author: email@example.com
Revised: 28 November 2001
Accepted: 12 December 2001
Published online: 15 April 2002
Thermally stimulated current measurements have been performed on polycrystalline layers of lead iodide grown from solution. Several TSC peaks or bands have been observed at temperatures of 100 K, 195–220 K, 230–240 K and 270–300 K. Comparison with PbI2 single crystal shows that the polycrystalline structure of the material introduces additional defects. In contrast the defect currently found in single crystal and attributed to the lead vacancy has not been clearly evidenced in the polycrystalline layers. The position and relative intensity of the peaks can be modified by Ag doping and thermal annealing. On the other hand, only small differences resulting from the anisotropy of the material have been observed depending on the orientation of the electric field with regards to the grains orientation.
PACS: 71.55.Ht – Other nonmetals / 72.20.Jv – Charge carriers: generation, recombination, lifetime, and trapping / 81.05.Hd – Other semiconductors
© EDP Sciences, 2002
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.